Fabricating pillar solder bump

ABSTRACT

A substrate bonding method is able to reliably bond substrates while avoiding a reduction in yield made worse by finer pitches. The substrate bonding method can include: forming an adhesive resin layer on a surface of a first substrate on which a pad has been formed; forming an opening on the adhesive resin layer above the pad; filling the opening with molten solder to form a pillar-shaped solder bump; and applying heat and pressure to the first substrate and a second substrate while a terminal formed on the second substrate is aligned with the solder bump.

CROSS REFERENCE TO RELATED APPLICATION

This application is a continuation of co-pending U.S. patent application Ser. No. 14/548,583, filed Nov. 20, 2014, which claims priority to Japan Patent Application No. 2013-247505, filed Nov. 29, 2013, the contents of which are incorporated herein in its entirety.

BACKGROUND

The present disclosure relates to a substrate bonding method, and more specifically to the formation of bumps using an adhesive resin, and to bonding a substrate using these bumps.

Methods for mounting chips on substrates known as “flip-chip techniques,” in which the bottom surface of a die and a substrate are connected via bumps arranged in the form of an array, are conventionally well-known. Among these techniques, the widely used controlled collapse chip connection (C4) technique, which uses solder balls as bumps. In the C4 technique, the solder bumps on the electrode pads on the bottom surface of the die are aligned with the substrate terminals, the solder is then melted, and the electrode pads on the bottom of the die are now connected electrically to the substrate terminals. Finally, the gap between the substrate and the die are filled with an under fill agent to secure the die.

However, these solder bumps have become finer as chips have become more highly integrated, and the pitch has become narrower. As a result, the gap between chips and substrates has narrowed, and under fill agents have become difficult to use.

In order to ensure that there is a sufficient gap between chips and substrates, the use of Cu pillar bumps which form solder bumps on copper columns (pillars) formed using a plating technique has been studied. However, there is a problem with these Cu pillar bumps.

First, the elastic modulus of copper is more than three times that of solder materials, and the yield stress is more than eight times that of solder materials. As a result, the thermal stress that occurs when a chip is bonded to a substrate (for example, the stress that occurs due to the difference in thermal expansion coefficients between a silicon chip and an organic substrate) cannot be sufficiently buffered. As a result, the chip is subjected to a significant amount of thermal stress, and cracks develop in wiring layers using dielectric interlayer insulating film which has low mechanical strength. This decreases yields. Second, copper pillar bumps are formed using electrolytic plating, which causes a variation in the height of the bumps. As a result, the bonding ability of the bumps and substrate terminals becomes unstable. These problems have been exacerbated by finer pitches.

SUMMARY

The present disclosure provides a substrate bonding method comprising the steps of: forming an adhesive resin layer on a surface of a first substrate, on which a pad has been formed; forming an opening on the adhesive resin layer above the pad; filling the opening with molten solder to form a pillar-shaped solder bump; and applying heat and pressure to the first substrate and a second substrate, while a terminal formed on the second substrate is aligned with the solder bump.

The present disclosure is able to provide a substrate bonding method which is able to reliably bond substrates, while avoiding reductions in yield exacerbated by finer pitches.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

FIG. 1A a substrate is prepared with a plurality of electrode pads, according to an embodiment.

FIG. 1B an adhesive resin layer is formed on the surface of the prepared substrate, according to an embodiment.

FIG. 1C the adhesive resin layer is patterned to form openings above the pads on the prepared substrate, according to an embodiment.

FIG. 1D the openings in the resin layer are filled with molten solder, according to an embodiment.

FIG. 1E the molten solder solidifies inside the openings forming pillar-shaped bumps according to an embodiment.

FIG. 2A a substrate with formed pillar-shaped bumps is diced to form a die, according to an embodiment.

FIG. 2B the die is aligned with pads of a substrate such that the pillar-shaped bumps are lined up with the pads of the substrate, according to an embodiment.

FIG. 2C heat and pressure are applied to bond the die to the substrate, according to an embodiment.

FIG. 3 is a set of graphs showing the temperature profile, and the bonding pressure profile, in the bonding step according to an embodiment.

FIG. 4 is a diagram showing the manner in which substrates, on which solder pillar bumps structures have been formed, are bonded.

FIG. 5A is a conceptual diagram for the C4 technique, according to an embodiment.

FIG. 5B is a conceptual diagram used to explain the results of the substrate bonding method, according to an embodiment.

FIG. 6 is a conceptual diagram used to explain the results of the substrate bonding method, according to an embodiment.

FIG. 7A is a cross-sectional view of an adhesive resin layer in which solder pillar bumps of a circle shape and heat-dissipating structures of a star-shape have been formed simultaneously.

FIG. 7B is a cross-sectional view of an adhesive resin layer in which solder pillar bumps of a rectangle shape and heat-dissipating structures of a cross-shape have been formed simultaneously.

FIG. 7C is a cross-sectional view of an adhesive resin layer in which solder pillar bumps of a circle shape and heat-dissipating structures of a cross-shape have been formed simultaneously.

FIG. 8A is a cross-sectional view of pattern 1 where an adhesive resin layer in which solder pillar bumps of a certain size have been formed in a rectangle shape for heat dissipation testing.

FIG. 8B is a cross-sectional view of pattern 2 where an adhesive resin layer in which solder pillar bumps of a certain size have been formed in a rectangle shape for heat dissipation testing.

FIG. 8C is a cross-sectional view of pattern 3 where an adhesive resin layer in which solder pillar bumps of a certain size have been formed in a rectangle shape and heat-dissipating structures of variable size and distance for heat dissipation testing.

DETAILED DESCRIPTION

The following is an explanation of an embodiment of the present disclosure with reference to the drawings. It should be understood that there is no intent to limit the scope of the present disclosure to the embodiment shown in the drawings. In the drawings described below, the same reference signs are used to denote the same elements unless otherwise noted.

Each of the diagrams referenced below has been exaggerated as necessary to aid in the explanation of the present disclosure and may not be to scale. In each of the diagrams, depiction of certain aspects of the configuration not directly related to the present disclosure, such as wiring, and under bump metal (UBM) have been omitted.

FIG. 1 is a diagram schematically showing the steps of the bump forming method according to this disclosure. The following is an explanation of the steps in the bump forming method of the present embodiment with reference to FIG. 1.

In the present embodiment, as shown in FIG. 1A, a substrate 10 is first prepared in which a plurality of electrode pads 12 that have been formed on the surface. The substrate 10 in the present embodiment can be made of any type of rigid or flexible material on which a plurality of electrode pads 12 can be formed. Examples include silicon substrates, organic substrates, and ceramic substrates. The substrate 10 can be also any type of substrate on which a plurality of electrode pads can be formed. Examples include dies diced from a wafer, wafers processed for wafer level chip size packages (WL-CSP), interposers for rewiring, main substrates, and package substrates.

In the present embodiment, as shown in FIG. 1B, an adhesive resin layer 13 is then formed on the surface of the prepared substrate 10 (the surface on which the electrode pads 12 have been formed). More specifically, a thermosetting resin composition is applied uniformly over the surface of the substrate 10 using any technique common in the art, such as spin coating. The resin is temporarily cured to form an adhesive resin layer 13. In the present embodiment, the adhesive resin layer 13 is thermally adhesive, and preferably photosensitive.

In the present embodiment, as shown in FIG. 1C, the adhesive resin layer 13 is patterned to form openings over the electrode pads 12 (referred to simply as pads 12 below). This patterning can be performed using any technique common in the art, for example, laser application or dry etching. When the adhesive resin layer 13 is photosensitive, the patterning can be patterned using exposure to light and development. As a result of patterning, openings 14 are formed directly above the pads 12, and the top surface of the pads 12 are exposed.

In the present embodiment, an injection molding technology is then used to fill the openings 14 with molten solder. The solder material can be a lead-free solder using tin, indium, a tin alloy, or an indium alloy that contains Ag, Cu, Zn, Bi, In, Sb, Ni, Co, Ge and/or Fe.

In the present embodiment, the molten solder filling step can be performed using injection molded soldering (IMS). FIG. 1D shows a molten solder filling step performed using the IMS technique. Here, a filling head 50 including a reservoir 52 for holding the molten solder, a channel 54, and a discharge slot 56, moves in a horizontal direction while making substantial contact with the adhesive resin layer 13. As this is occurring, the molten solder is pushed through the channel 54 below via a port 58 by applying back pressure on the reservoir 52. As a result, the molten solder is supplied directly to the opening 14 directly beneath the discharge slot 56 and the opening 14 is filled.

The molten solder filling of the openings 14 via the discharge slot 56 later solidifies inside the openings 14. As a result, and as shown in FIG. 1E, a pillar-shaped bump 16 (referred to below as a solder pillar bump 16) is formed directly above each pad 12. In the present embodiment, the head of each solder pillar bump 16 has a convex shape because of surface tension. When solidified, they protrude somewhat above the top surface of the adhesive resin layer 13.

The solder pillar bump forming method was explained above with reference to FIG. 1. The following is an explanation of the substrate bonding method, using these solder pillar bumps, with reference to FIG. 2.

FIG. 2 is a diagram schematically showing the steps of the substrate bonding method using solder pillar bumps according to an embodiment. In the present embodiment, a substrate is first prepared in which solder pillar bumps have been formed. Here, as shown in FIG. 2A, the substrate is a wafer that has been processed for WL-CSP, and the substrate on which solder pillar bumps 16 have been formed, is diced to obtain a die 20.

Next, the substrate 30 on which the die 20 is to be bonded is prepared. The substrate 30 in the present embodiment can be any substrate on which a plurality of terminals 32 can be formed to connect to the solder pillar bumps. Because many of the details are the same as those in the substrate 10 described above, further explanation has been omitted.

In the present embodiment, the die 20 and the substrate 30 are next bonded using the flip-chip technique. More specifically, as shown in FIG. 2B, the surface of the die 20 on which the solder pillar bumps have been formed is facing downward, and the positions of the solder pillar bumps 16, are aligned with the positions of the terminals 32, on the substrate 30. Afterwards, as shown in FIG. 2C, heat and pressure are applied to bond the die 20, and the substrate 30.

The following is an explanation, with reference to FIG. 3, of the relationship between temperature and bonding pressure in the bonding step described above.

FIG. 3 shows the correspondence between the temperature profile and the bonding pressure profile in the bonding step. In the present embodiment, as shown in FIG. 3, sufficient pressure is first applied at a temperature below the melting point (m.p.) of the solder material constituting the solder pillar bumps 16, and the die 20 and the substrate 30 are pressure-bonded. At this stage, the solder pillar bumps 16 formed on the die 20 have not melted, and the adhesive resin layer 13 does not exhibit thermal adhesiveness.

Afterwards, the bonding pressure is lowered somewhat, the temperature is raised above the melting point (m.p.) of the solder material, and reflow processing is performed. At this stage, the solder pillar bumps 16 formed on the die 20 have melted, and spread to the terminals 32 on the substrate 30. Also, the adhesive resin layer 13 exhibits thermal adhesiveness, and adheres to the surface of the substrate 30, on which the terminals 32 have been formed.

In the subsequent cooling step, the molten solder and the bonded layer of the adhesive resin layer 13 are solidified. As a result, the pads 12 and terminals 32 are connected electrically via the solder pillar bumps 16, and the die 20 is reliably secured to the substrate 30.

In FIG. 2 described above, electrode pads are formed as the terminals 32 on the substrate 30. However, this is merely an example. The terminals connected to the tips of the solder pillar bumps 16 can be bumps instead of electrode pads. FIG. 4 shows substrates on which the solder pillar bumps described above have been formed and which have been bonded to each other using the flip-chip technique. If an adhesive resin layer 13 has been formed on substrate 10, the resin layer 43 formed on substrate 30 does not have to be thermally adhesive.

A substrate bonding method using solder pillar bumps was explained above. The following is an explanation of the effects of the substrate bonding method of the present disclosure.

First, the adhesive resin layer 13 used to form the solder pillar bumps 16 simultaneously bonds the substrate and functions as an under fill agent. As a result, an under fill agent adding step is not required which is an advantage from the standpoint of cost.

Second, it allows for finer pitches than the controlled collapse chip connection (C4) technique. This will be explained with reference to FIG. 5.

In the C4 technique, as shown in FIG. 5A, the distance between adjacent solder balls decreases and the risk of contact between solder balls increases as the pad pitch P is narrowed. Because the diameter of solder balls also decreases as the pad pitch P becomes narrower, a sufficient gap between the two bonded substrates cannot be ensured and, as a result, it is difficult to fill the gap with an under fill agent. This causes problems such as increased processing times and solder shorts due to a lack of under filling. For these reasons, use of the C4 technique is limited with respect to finer pitches.

However, in the present disclosure, as shown in FIG. 5B, there is an adhesive resin layer 13 between adjacent solder pillar bumps 16 even when the distance between bumps becomes smaller because of a narrower pad pitch P. As a result, there is no need to be concerned about solder shorts.

Third, because the elastic modulus of the solder metal constituting the solder pillar bumps 16 is one-third that of copper, the thermal stress occurring between substrates can be sufficiently buffered, as compared to the structure of the prior art in which a gap is insured between substrates using Cu pillar bumps. As a result, cracking is less likely to occur, and yields are improved even for substrates using more porous dielectric interlayer insulating film in the wiring layers.

Fourth, no resin remains on the heads of the solder pillar bumps 16 in the configuration obtained using the bump forming method, and resin does not become caught during the substrate bonding process.

Fifth, unlike Cu pillar bumps which tend to vary in bump height, the bump height of solder pillar bumps is easily aligned. Also, as shown in FIG. 6, the heads 16 protrude somewhat above the top surface of the adhesive resin layer 13 and make reliable contact with the substrate terminals 32. As a result, more reliable bonding occurs.

As explained above, the present disclosure can adequately address finer pitches which will become more prevalent in the future.

Here, one problem that is exacerbated by higher integration such as finer pitches is the so-called “hot spot” problem. The present disclosure proposes a method in which “heat-dissipating structures” are formed at the same time as the bumps as a hot spot countermeasure.

The method used to form heat-dissipating structures in the present disclosure is essentially the same as the method used to form the solder pillar bumps explained above. When openings are formed for the solder pillar bumps in the adhesive resin layer formed on the substrate, openings are also formed for the heat-dissipating structures in locations that do not interfere electrically with the solder pillar bumps. Afterwards, the solder pillar bumps and heat-dissipating structures are formed at the same time by filling each opening with solder and allowing the solder to cool. At this time, the heat-dissipating structures are connected thermally to the two bonded substrates without affecting the device electrically.

FIG. 7 is a set of cross-sectional views of an adhesive resin layer in which solder pillar bumps and heat-dissipating structures have been formed simultaneously. FIG. 7A shows an example in which column-shaped heat-dissipating structures 18A with a star-shaped cross-section, are formed between solder pillar bumps 16A with a round cross-section. FIG. 7B shows an example in which column-shaped heat-dissipating structures 18B with a cross-shaped cross-section, are formed between solder pillar bumps 16B with a rectangular cross-section. FIG. 7C shows an example in which column-shaped heat-dissipating structures 18C with a cross-shaped cross-section, are formed between solder pillar bumps 16C with a round cross-section.

When heat-dissipating structures are formed inside the adhesive resin layer, thermal conductivity increases in the thickness direction (Z direction) between two substrates bonded via the adhesive resin layer. When a plurality of connected heat-dissipating structures 18 extend in the planar directions, the thermal conductivity can be increased in the planar directions (XY directions) in addition to the thickness direction (Z direction).

Table 1 includes the theoretical values for thermal conductivity in the thickness direction (Z direction), and the planar directions (XY directions), when solder pillar bumps 16 and heat-dissipating structures 18 are formed in Patterns 1-3 shown in FIGS. 8A, 8B, and 8C. These theoretical values were calculated using 50 W/(m·K) as the thermal conductivity of the solder and 0.5 W/(m·K) as the thermal conductivity of the resin layer.

TABLE 1 Thickness Planar Direction (z) Directions (xy) Pattern 1 12.9 W/(m · K) 1.0 W/(m · K) Pattern 2 24.8 W/(m · K) 1.6 W/(m · K) Pattern 3 W = 10 um 22.3 W/(m · K) 5.8 W/(m · K) S = 20 um Pattern 3 W = 20 um 30.7 W/(m · K) 11.0 W/(m · K)  S = 15 um

When the theoretical values of Pattern 1 and Pattern 2 are compared, it is clear that the thermal conductivity in the thickness direction (Z direction) improves as the size of the solder pillar bumps 16 is increased, and the thermal conductivity in the planar directions (XY directions) is improved somewhat when the gaps between bumps are narrowed along with the increased size of the bumps. When the theoretical values of Pattern 1 and Pattern 3 are compared, it is clear that the thermal conductivity is improved significantly in both the thickness direction (Z direction) and the planar directions (XY directions) when lattice-like heat-dissipating structures 18 extend in the planar directions.

When the substrate bonding method of the present disclosure described above is used, both lower costs and higher yields can be realized, and semiconductor devices can be manufactured with more reliable bonding.

The present disclosure was explained using a specific embodiment, but the present disclosure is not limited to these specific embodiments and examples. The present disclosure can be altered in any way conceivable by a person of skill in the art, including other embodiments, additions, modifications, and deletions. Any mode or aspect realizing the actions and effects of the present embodiment is within the scope of the present disclosure. 

What is claimed is:
 1. A bump forming method comprising: forming an adhesive resin layer on a surface of one or more electrode pads on a first substrate; forming a first opening on the adhesive resin layer above an electrode pad from the one or more electrode pads; forming a second opening on the adhesive resin layer not above the electrode pad; forming a pillar-shaped solder bump by filling the first opening above the electrode pad with molten solder; and forming a heat-dissipating structure solder bump by filling the second opening not above the electrode pad with molten solder.
 2. The method of claim 1, wherein the adhesive resin layer is a photosensitive adhesive resin layer.
 3. The method of claim 2, wherein forming the first opening and the second opening includes: exposing the photosensitive adhesive resin layer to light to form the opening.
 4. The method of claim 1, wherein the forming a pillar-shaped solder bump further comprises solidifying the molten solder.
 5. The method of claim 1, wherein the first substrate is selected from the group consisting of: silicon, organic, and ceramic substrates.
 6. The method of claim 1, wherein forming an adhesive resin layer includes: applying the adhesive resin layer uniformly over the surface of one or more electrode pads in the first substrate using spin coating.
 7. The method of claim 1, wherein filling the opening with molten solder includes: filling the opening using injection molded soldering (IMS).
 8. The method of claim 1, wherein the molten solder is selected from: a tin alloy, and an indium alloy.
 9. The method of claim 8, wherein the tin alloy contains at least one selected from the group consisting of: Ag, Cu, Zn, Bi, In, Sb, Ni, Co, Ge and Fe.
 10. The method of claim 1, wherein the heat-dissipating structure solder bump is formed in a star-shaped cross-section.
 11. The method of claim 1, wherein the heat-dissipating structure solder bump is formed in a column shape with a cross-shaped cross-section.
 12. The method of claim 11, wherein the forming of the cross-shaped cross-section causes the heat-dissipating structure solder bump to be oriented in a planar orientation.
 13. The method of claim 11, wherein the cross-shaped cross-section of the heat-dissipating structure solder bump is formed as a lattice type structure.
 14. The method of claim 1, wherein forming the first opening and the second opening includes using a laser to etch the resin layer.
 15. The method of claim 1, wherein forming the first opening and the second opening includes dry etching of the resin layer.
 16. An apparatus for forming a bump comprising: a spin coater configured to: form an adhesive resin layer on a surface of one or more electrode pads on a first substrate; an etching device configured to: form a first opening on the adhesive resin layer above an electrode pad from the one or more electrode pads, and form a second opening on the adhesive resin layer not above the electrode pad; and an injection mold soldering device configured to: form a pillar-shaped solder bump by filling the first opening above the electrode pad with molten solder; forming a heat-dissipating structure solder bump by filling the second opening not above the electrode pad with molten solder.
 17. The apparatus of claim 16, wherein the heat-dissipating structure solder bump is formed in a star-shaped cross-section.
 18. The apparatus of claim 16, wherein the heat-dissipating structure solder bump is formed in a column shape with a cross-shaped cross-section. 